Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	1170 - 1450 MPa	170000 - 210000 psi
Materion Beryllium Copper Alloy M25 Wire; 1/2HT (TH02) Temper; 1.3-12.7 mm Diameter (UNS C17300) Treatment required for max strength: 1.5 hrs @ 315-330Â°C Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed..
Tensile Strength, Yield	1170 MPa	170000 psi	Tempered at 900Â°F, 1hr
Latrobe LescalloyÂ® 15-5 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 15-5 VAC-ARC steel is a precipitation hardening martensitic stainless steel commonly considered to be a compositional modification of 17-4 with minimal delta ferrite. A wide range of mec..
Tensile Strength, Yield	>= 1170 MPa @Strain 0.200 %	>= 170000 psi @Strain 0.200 %	H900 Condition - 480Â°C at 1 hr
Latrobe LescalloyÂ® 15-5 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 15-5 VAC-ARC steel is a precipitation hardening martensitic stainless steel commonly considered to be a compositional modification of 17-4 with minimal delta ferrite. A wide range of mec..
Tensile Strength, Yield	1170 - 1450 MPa	170000 - 210000 psi
Materion Beryllium Copper Alloy 25 Wire; 1/2HT (TH02) Temper; 1.3-12.7 mm Diameter (UNS C17200) Treatment required for max strength: 1.5 hrs @ 315-330Â°C Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed..
Tensile Strength, Yield	1170 MPa @Strain 0.200 %	170000 psi @Strain 0.200 %
Haynes 214Â® alloy, 30% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	1170 MPa @Strain 0.200 %	170000 psi @Strain 0.200 %
Haynes 556Â® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	>= 1170 MPa @Temperature 900 Â°C, Time 3600 sec	>= 170000 psi @Temperature 1650 Â°F, Time 1.00 hour
Schmolz + Bickenbach UGIMAÂ® 630 Stainless Steel Bar Description: 630 UGIMAÂ® is an improved machining martensitic precipitation hardenable grade produced only by Ugitech. It is identical in every way to standard type 630 (17-4), except with respect..
Tensile Strength, Yield	1170 MPa @Strain 0.200 %	170000 psi @Strain 0.200 %	Typical
TIMET 10-2-3 Titanium Alloy (Ti-10V-2Fe-3Al), Aged Billet/Bar per ASTM 4984 High-Strength Forging Alloy.Industry Specifications: USA Aerospace: AMS 4984.Features: A readily forgeable alloy that offers excellent combinations of strength, ductility, fracture toughness and hi..
Tensile Strength, Yield	1170 MPa	170000 psi
Elgiloy® Co-Cr-Ni Alloy, Strip, 40% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati..
Tensile Strength, Yield	1170 MPa	170000 psi
ATI Allvac® 718Plus™ Nickel Superalloy Allvac 718Plus alloy (UNS N07818) is a precipitation hardened nickel-base material that exhibits high temperature tensile strength and stress rupture performance. This alloy is designed to have the..
Tensile Strength, Yield	>= 1170 MPa	>= 170000 psi
Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H1050 (H1050) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.