Polymer Property : Tensile Strength, Yield = 30200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	208 MPa	30200 psi	ASTM D638
Techmer ES HiFillÂ® PA6/6 GF43 L BK001 43% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 43% Filler by WeightAdditive: Lubricant Features: Lubricated Appearance: BlackTPCI# 7176101Information provi..
Tensile Strength, Yield	208 MPa	30200 psi	ASTM D638
Techmer ES HiFillÂ® PA6/6 GF43 L BKN001 43% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 43% Filler by WeightAdditive: Lubricant Features: Lubricated Appearance: BlackProcessing Method: Injection M..
Tensile Strength, Yield	208 MPa	30200 psi	ASTM D638
Techmer ES HiFillÂ® PA6/6 GF43 LE BK 43% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 43% Filler by WeightAdditive: Lubricant Features: Lubricated and Low ExtractablesAppearance: BlackInformatio..
Tensile Strength, Yield	208 MPa	30200 psi	ASTM D638
Techmer ES HiFillÂ® PA6/6 GF45 L BK 45% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 45% Filler by WeightAdditive: Lubricant Features: Lubricated Appearance: BlackProcessing Method: Injection M..
Tensile Strength, Yield	208 MPa	30200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA LNP* THERMOCOMP* UF006H is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare.
Tensile Strength, Yield	208 MPa	30200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA (Asia Pacific) LNP* Thermocomp* UF006H is a compound based on Polyphthalamide resin containing Glass Fiber.
Tensile Strength, Yield	208 MPa	30200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Verton RV008ESV PA 66 40% long glass fiber filled PA66 Verton Xtreme XCThis data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield	208 MPa	30200 psi	ISO 527
Eurostar Star L PA66 30Y D51 PA66, Carbon Fiber Filled, Injection Molded Star L PA66 30Y D51 is a PTFE Lubricated, Carbon Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
Tensile Strength, Yield	208 MPa @Strain 0.200 %, Temperature 427 °C	30200 psi @Strain 0.200 %, Temperature 801 °F
Carpenter Gall-Tough PLUS™ Stainless, Annealed Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 4..
Tensile Strength, Yield	208 MPa	30200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP VERTON RX00327 PA 66 LNP* VERTON* RX00327 is a compound based on Nylon 66 resin containing proprietary fillers. Added feature of this material is: Structural.