Polymer Property : Tensile Strength, Yield = 720 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	720 - 860 MPa	104000 - 125000 psi
Materion Brush 60â„¢ HT Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 96%Stress Relaxation afte..
Tensile Strength, Yield	720 MPa @Strain 0.200 %	104000 psi @Strain 0.200 %
Haynes 214Â® alloy, sheet, 32 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	720 MPa @Strain 0.200 %	104000 psi @Strain 0.200 %
Haynes 625 alloy, plate after 4000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Yield	720 MPa @Strain 0.200 %, Temperature 650 Â°C	104000 psi @Strain 0.200 %, Temperature 1200 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 105 A precipitation-hardenable nickel-cobalt-chromium alloy with an addition of molybdenum for solid-solution strengthening. The relatively high aluminum content enhances both strength (through greater..
Tensile Strength, Yield	720 MPa @Strain 0.200 %, Temperature 550 Â°C	104000 psi @Strain 0.200 %, Temperature 1020 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 115 A precipitation-hardenable nickel-chromium-cobalt alloy with an addition of molybdenum for solid-solution strengthening. It is similar to NIMONIC alloy 105 but has higher levels of aluminum and tit..
Tensile Strength, Yield	720 MPa @Strain 0.200 %, Temperature 650 Â°C	104000 psi @Strain 0.200 %, Temperature 1200 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy PK33 A nickel-chromium-cobalt alloy that is precipitation hardenable and also contains a relatively high (7%) level of molybdenum for solid-solution strengthening. It has an exceptional combination of h..
Tensile Strength, Yield	>= 720 MPa @Strain 0.200 %	>= 104000 psi @Strain 0.200 %
CLAL-MSX NICLAFOR® 1000 TH2 Quenched/Cold Rolled/Precipitation Heat Treated, Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Yield	720 MPa	104000 psi
Elgiloy® Co-Cr-Ni Alloy, Strip, 10% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High ..
Tensile Strength, Yield	720 MPa @Temperature 550 °C	104000 psi @Temperature 1020 °F	R<sub>p</sub>02
Assab Steels 8407 2M Hot Work Steel ASSAB 8407 is a chromium-molybdenum-vanadium-alloyed steel which is characterized by: Good resistance to abrasion at both low and high temperatures. High level of toughness and ductility Uniform ..
Tensile Strength, Yield	720 MPa @Temperature 550 °C	104000 psi @Temperature 1020 °F	R<sub>p</sub>02
Assab Steels 8407 SUPREME Hot Work Steel 8407 SUPREME is characterized by:High level of resistance to thermal shock and thermal fatigueGood high temperature strengthExcellent toughness and ductility in all directionsGood machinability and ..