Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ASTM D638 |
NYCOA 1637 PA 6 plasticized and heat stabilized extrusion grade for the wire jacketing industry to 7,000+ fpm. UL Flammability Component listing for use as cable jacketing.Information provided by NYCOA, Inc. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer Lexan* DMX1132 is a high flow polycarbonate copolymer resin with improved ammonia resistance over regular polycarbonate resin. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Lubricomp DFP22 PC LNP* DFP22 is a Polycarbonate base resin containing glass fiber and PTFE/Silicone Lubricants. Characteristic of this grade is: Internally Lubricated.This data was supplied by SABIC-IP for the Amer.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer (Asia Pacific) Lexan* DMX1132 is a high flow polycarbonate copolymer resin with improved ammonia resistance over regular polycarbonate resin. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer (Europe-Africa-Middle East) Lexan* DMX1132 is a high flow polycarbonate copolymer resin with improved ammonia resistance over regular polycarbonate resin.This data was supplied by SABIC-IP for the Europe-Africa-Middle East reg.. |
|||
Tensile Strength, Yield | 73.0 MPa @Temperature 23.0 °C |
10600 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 527UVE RD402 Acetal Homopolymer
(Unverified Data**) Delrin® 527UVE RD402 (formerly DE20556) is a medium viscosity acetal homopolymer with UV stabilizers, pigmented red, having extremely low VOC emissions, developed for automotive interior applicatio.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PX9406P PPE+HIPS (Asia Pacific) Nonbrominated, nonchlorinated, flame retarded. Improved productivity and reliability. 125dc HDT. UL94 V-0 rated. Electrical applications. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp EL004 PEI LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp EL004 PEI (Asia Pacific) LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pac.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527 |
SABIC Innovative Plastics LNP Lubricomp EL004 PEI (Asia Pacific) LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pac.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL V02570 PPE+HIPS Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL V02570 PPE+HIPS (Asia Pacific) Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL V02570 PPE+HIPS (Europe-Africa-Middle East) Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK LNP* LUBRICOMP* LL004E is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK (Asia Pacific) LNP* Lubricomp* LL004E is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK (Asia Pacific) LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® SHF4910 PBT (Europe-Africa-Middle East) 6.5% glass reinforced, Super High Flow, flame retardant PBT. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 527UVE RD402 Acetal (POM)
(Unverified Data**) UV Stabilized Medium Viscosity Acetal Homopolymer with Very Low Emissions Delrin 527UVE RD402 (formerly DE20556) is a medium viscosity acetal homopolymer with UV stabilizers pigmented red with very .. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 588P NC010 Acetal (POM) Nucleated Medium Viscosity Acetal HomopolymerInformation provided by DuPont Performance Polymers |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 500PE NC010 Acetal (POM)
(Unverified Data**) Medium Viscosity Acetal Homopolymer with Very Low Emissions Delrin 500PE NC010 (formerly DE20578) is a medium viscosity acetal homopolymer an enhanced version of Delrin 500P with very low VOC emissi.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 23°C, 50% RH; ASTM D638 |
Asahi Kasei Xyron® 640Z Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527 |
Ascend Performance Materials Vydyne® R220 Nylon 66, 40% mineral reinforced, Conditioned Vydyne® R220 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in natural, it is an injection-molding grade formulated to retain the inherent processing adva.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527 |
Ascend Performance Materials Vydyne® R220/R228 Nylon 66, 40% Mineral Reinforced, Conditioned (2.5% Moisture) Vydyne® R220 is a 40% mineral reinforced Nylon 66 resin formulated for improved impact strength. Also available in black as R228. It is an injection molding grade formulated to retain the inherent .. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R228 Nylon 66, 40% Mineral Reinforced, Conditioned Vydyne® R228 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in black, it is an injection-molding grade formulated to retain the inherent processing advant.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 50mm/min; ISO 527 |
BASF Ultramid® B29 HM 01 PA6 (Dry) Ultramid B29 HM 01 is a medium viscosity , heat stabilized, PA6 universal wire jacketing resin offering excellent performance through the range of THHN, THWN, and TFFN constructions. It possesses a.. |
|||
Tensile Strength, Yield | 73.0 MPa @Temperature 23.0 °C |
10600 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 588P NC010 Acetal Homopolymer
(Unverified Data**) Delrin® 588P NC010 is a medium viscosity acetal homopolymer resin for injection molding. It has good thermal stability, and modifications for more precise molding (reduced warpage, good dimensiona.. |
|||
Tensile Strength, Yield | 73.0 MPa @Temperature 23.0 °C |
10600 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® FG311DP NC010 Acetal Homopolymer
(Unverified Data**) Delrin® FG311DP is a medium-high viscosity acetal homopolymer, with improved thermal stability and modifications for more precise molding. It has been developed for consideration into applications .. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL FE8000S PPE+PS (Asia Pacific) Noryl* FE8000S resin is an unfilled modified polyphenylene ether resin designed for fluid handling applications. This resin is suitable for multiple conversion routes and will be available in custom.. |
|||
Tensile Strength, Yield | 73.0 MPa | 10600 psi | ASTM D638 |
LyondellBasell Higlass PF062-2 Polypropylene Homopolymer, 20% Glass Fiber Key Features: high melt flow, medium high modulus, chemically coupled, glass fiber-reinforced polypropylene homopolymer, high rigidity, high strength, excellent processabilityApplications: appliance.. |