Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 6.35 GPa | 921 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP WFL33 PBT LNP* LUBRICOMP* WFL33 is a compound based on PBT containing 15% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Tensile Modulus | 6.35 GPa | 921 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PF003 PA 6 LNP THERMOCOMP* PF003 is a compound based on Nylon 6 resin containing 15% Glass Fiber. |
|||
Tensile Modulus | 6.35 GPa | 921 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PF003 PA 6 (Asia Pacific) LNP* THERMOCOMP* PF003 is a compound based on Nylon 6 resin containing Glass Fiber. |