Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 4.34 GPa | 629 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Faradex ES003DE PEI LNP* Faradex* ES003DE is a Polyetherimide resin containing stainless steel fibers. Characteristics of this grade are EMI/RFI Shielding.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Modulus | 4.34 GPa | 629 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP FARADEX ES003E PEI LNP* FARADEX* ES003E is a Polyetherimide resin containing 15% Stainless Steel Fibers. Added feature of this grade is: EMI/RFI Shielding. |
|||
Tensile Modulus | 4.34 GPa | 629 ksi | 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp DFL329EF PC LNP LUBRICOMP* DFL329EF is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant.This data was supplied by .. |
|||
Tensile Modulus | 4.34 GPa | 629 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM AR9100 PEI (Asia Pacific) 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
Tensile Modulus | 4.34 GPa | 629 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP AX90213 ABS LNP* THERMOCOMP* AX90213 is a compound based on ABS resin containing Glass Fiber. |
|||
Tensile Modulus | 4.34 GPa | 629 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP AX90213 ABS (Asia Pacific) LNP* Thermocomp* AX90213 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. |
|||
Tensile Modulus | 4.34 GPa | 629 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6 Noryl GTX* GTX675 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to a.. |
|||
Tensile Modulus | 4.34 GPa @Temperature 23.0 °C |
629 ksi @Temperature 73.4 °F |
EN ISO 527 |
Ensinger TECASINT 1041 Polyimide, 30% MoS2 Filled (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Tensile Modulus | 4.34 GPa | 629 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL329 PC LNP LUBRICOMP* DFL329 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated. |
|||
Tensile Modulus | 4.34 GPa | 629 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM AR9100 PEI 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |