Polymer Property : Tensile Modulus = 7.31 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	7.31 GPa	1060 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRILOY DX08333 PC (Asia Pacific) LNP Lubriloy* DX08333 is an internally lubricated compound based on Lexan* Polycarbonate resin. Added features of this material include: ESD Safe, PTFE-free Wear & Friction solution and balanced mec..
Tensile Modulus	7.31 GPa @Temperature 100 Â°C	1060 ksi @Temperature 212 Â°F	4; ISO 527-2
Solvay Specialty Polymers AmodelÂ® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Dry) AmodelÂ® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high stre..
Tensile Modulus	7.31 GPa @Temperature 150 Â°C	1060 ksi @Temperature 302 Â°F	4; ISO 527-2
Solvay Specialty Polymers AmodelÂ® AS-1566 HS Polyphthalamide (PPA), 65% GlassMineral (Dry) AmodelÂ® AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifica..
Tensile Modulus	7.31 GPa	1060 ksi	cond; ISO 527-1/-2
DSM Akulon® Ultraflow K-FPG8 PA6-I-GF40 Glass Reinforced, High flow
Tensile Modulus	7.31 GPa @Temperature 100 °C	1060 ksi @Temperature 212 °F	ISO 527-2
Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA) (Unverified Data**) Amodel A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength..
Tensile Modulus	7.31 GPa @Temperature 150 °C	1060 ksi @Temperature 302 °F	ISO 527-2
Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifically ..