Polymer Property : Tensile Modulus = 7.35 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	7.35 GPa	1070 ksi
Plastcom SLOVAMID 66 GF 15 GB 25 TS PA66, 15% glass fibre, 25% glass beads FeaturesPA 66 chemically reinforced with 15 % glass fibre and with the content of 25% glass beads, thermo stable. Improved anisotropy of shrinkage. The relation of the anisotropy to the mechanical p..
Tensile Modulus	7.35 GPa	1070 ksi
Radici Radilon® S RCV3515 (dry) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.
Tensile Modulus	7.35 GPa	1070 ksi
Radici Radilon® S RV350 (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.
Tensile Modulus	7.35 GPa	1070 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF004 PES LNP THERMOCOMP* JF004 is a compound based on Polyethersulfone resin containing 20% Glass Fiber.
Tensile Modulus	7.35 GPa	1070 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Asia Pacific) LNP* THERMOCOMP* JF004 is a compound based on Polyethersulfone resin containing Glass Fiber.
Tensile Modulus	7.35 GPa	1070 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Asia Pacific) LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Modulus	7.35 GPa	1070 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF004EXP PES LNP* THERMOCOMP* JF004EXP is a compound based on Polyethersulfone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding.
Tensile Modulus	7.35 GPa	1070 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF004EXP PES (Asia Pacific) LNP* Thermocomp* JF004EXP is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Modulus	7.35 GPa @Temperature -20.0 °C	1070 ksi @Temperature -4.00 °F	ISO 11403-1 -2
DuPont Performance Polymers Crastin® SK603 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) 20% Glass Reinforced Polybutylene Terephthalate Crastin SK603 NC010 is a 20% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont P..
Tensile Modulus	7.35 GPa	1070 ksi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® PLS FR95G15DH2 BK269 Nylon 6 15% Glass Reinforced Flame Retardant Heat Stabilized Polyamide Zytel PLSFR95G15DH2 BK269 is 15% glass reinforced flame retardant black PA using SHIELD Technology only from DuPont exceptional resista..
Tensile Modulus	7.35 GPa @Temperature 23.0 °C	1070 ksi @Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Zytel® PLUS PLSFR95G15DH2 BK269 Nylon (Unverified Data**) Zytel® PLSFR95G15DH2 BK269 is 15% glass reinforced, flame retardant black PA using SHIELD Technology, only from DuPont, exceptional resistance in hot air & hot engine oil.Information provided by Du..
Tensile Modulus	7.35 GPa	1070 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES LNP* THERMOCOMP* JF004E is a compound based on Polyethersulfone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding.