Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 8.81 GPa | 1280 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC LNP* Lubricomp* DFL16E is a compound based on Polycarbonate resin containing 30% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated, Easy Molding. |
|||
Tensile Modulus | 8.81 GPa | 1280 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC (Asia Pacific) LNP* Lubricomp* DFL16E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Easy Molding. |
|||
Tensile Modulus | 8.81 GPa | 1280 ksi | ISO 527 |
Polyram PlusTek PA7800G33 Nylon 6.6 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Impact Modified 33% Glass fiber reinforced, heat stabilized, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram. |