Polymer Property : Film Tensile Strength at Yield, TD = 37700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, TD	260 MPa	37700 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Mitsubishi HostaphanÂ® RN, 12 micron Nominal Thickness Universal Polyethylene Terephthalate Film HostaphanÂ® RN is a transparent, biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties. HostaphanÂ® RN is the standard product for..
Film Tensile Strength at Yield, TD	260 MPa	37700 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Mitsubishi HostaphanÂ® RN, 15 micron Nominal Thickness Universal Polyethylene Terephthalate Film HostaphanÂ® RN is a transparent, biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties. HostaphanÂ® RN is the standard product for..
Film Tensile Strength at Yield, TD	260 MPa	37700 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Mitsubishi HostaphanÂ® RN, 19 micron Nominal Thickness Universal Polyethylene Terephthalate Film HostaphanÂ® RN is a transparent, biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties. HostaphanÂ® RN is the standard product for..
Film Tensile Strength at Yield, TD	260 MPa	37700 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Mitsubishi HostaphanÂ® RN, 23 micron Nominal Thickness Universal Polyethylene Terephthalate Film HostaphanÂ® RN is a transparent, biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties. HostaphanÂ® RN is the standard product for..
Film Tensile Strength at Yield, TD	260 MPa	37700 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Mitsubishi HostaphanÂ® RN, 36 micron Nominal Thickness Universal Polyethylene Terephthalate Film HostaphanÂ® RN is a biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties.Applications:Films for industrial applicationsCoatingLamin..
Film Tensile Strength at Yield, TD	260 MPa	37700 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Mitsubishi HostaphanÂ® RN, 50 micron Nominal Thickness Universal Polyethylene Terephthalate Film HostaphanÂ® RN is a biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties.Applications:Films for industrial applicationsCoatingLamin..
Film Tensile Strength at Yield, TD	260 MPa	37700 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Mitsubishi HostaphanÂ® RN, 75 micron Nominal Thickness Universal Polyethylene Terephthalate Film HostaphanÂ® RN is a biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties.Applications:Films for industrial applicationsCoatingLamin..