Polymer Property : Film Tensile Strength at Break, TD = 30.4 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	30.4 MPa	4410 psi	ASTM D882
Lotte Chemical Titan TITANEX® LF1041 Linear low density polyethylene resin (discontinued **) LF1041 is a pelleted linear low density polyethylene resin formulated with antioxidant, high antiblock and slip agent. This product is used for blown film extrusion which offers outstanding toughne..
Film Tensile Strength at Break, TD	30.4 MPa	4410 psi	ASTM D882
Lotte Chemical Titan TITANEX® LF1043 Linear low density polyethylene resin (discontinued **) LF1043 is a pelleted linear low density polyethylene resin formulated with antioxidant, and antiblock agent. This product is used for blown film extrusion which offers outstanding toughness, extrud..
Film Tensile Strength at Break, TD	30.4 MPa	4410 psi	ASTM D882
Lotte Chemical Titan TITANEX® LF1044 Linear low density polyethylene resin (discontinued **) LF1044 is a pelleted linear low density polyethylene resin formulated with antioxidant. This product is used for blown film extrusion which offers outstanding toughness, extrudability and draw down..
Film Tensile Strength at Break, TD	30.4 MPa	4410 psi	500mm/min, Ultimate; ASTM D638
LG Chemical SEETEC EF320 Ethylene Vinyl Acetate Characteristics: Good Mechanical Properties and Good Optical PropertiesApplications: Agricultural FilmCAS No. 24937-78-8Information provided by LG Chemical
Film Tensile Strength at Break, TD	30.4 MPa	4410 psi	500mm/min, Ultimate; ASTM D638
LG Chemical SEETEC EF321 Ethylene Vinyl Acetate Characteristics: Good Mechanical Properties. Good Optical Properties. Additives : No Additive Applications: Agricultural FilmCSA No. 25895-47-0Information provided by LG Chemical
Film Tensile Strength at Break, TD	30.4 MPa	4410 psi	500mm/min, Ultimate; ASTM D638
LG Chemical SEETEC EF443 Ethylene Vinyl Acetate Characteristics: Good Mechanical Properties and Good Optical PropertiesApplications: Agricultural FilmCSA No. 24937-78-8Information provided by LG Chemical
Film Tensile Strength at Break, TD	30.4 MPa	4410 psi
Kuraray HYBRARÂ® CF4 Mono Layer Cast Film Description: HYBRARÂ® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRARÂ® is a special thermoplastic rubb..
Film Tensile Strength at Break, TD	30.4 MPa	4410 psi	25.4 microns; ASTM D882
Dow 118.01 Developmental Performance Polypropylene Polymer D118.01 Developmental Performance Polymer is a propylene-based resin intended for use in film, sheet extrusion and injection molding applications. Film and sheet produced from this resin offer impr..