Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi | ASTM D882 |
Westlake Hifor Xtreme SC74844 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74844 polymer is a high strength linear low density polyethylene designed for blown film extrusion that contains medium slip, high antiblock and processing aid. Films produce.. |
|||
Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi | ASTM D882 |
Westlake Hifor Xtreme SC74853 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74853 polymer is a high strength linear low density polyethylene designed for blown film extrusion that contains no slip, high antiblock and processing aid. Films produced wi.. |
|||
Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi | ASTM D882 |
Westlake Hifor Xtreme SC74858 Linear Low Density Polyethylene WESTLAKE HIFOR Xtreme SC74858 polymer is a high strength, good clarity linear low density polyethylene designed for blown film extrusion that contains no slip or antiblock and processing aid. Films .. |
|||
Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi | ASTM D882 |
Westlake Mxsten CV77512 Polyethylene Plastomer Mxsten CV plastomer CV77512 is a polyethylene plastomer designed for blown film extrusion that contains high slip, high antiblock and high processing aid additives. Films produced with this resin ex.. |
|||
Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi | ASTM D882 |
Westlake Mxsten CV77523 Polyethylene Plastomer Mxsten CV plastomer CV77523 is a polyethylene plastomer designed for blown film extrusion that contains high slip, very high antiblock and polymer processing aid additives. Films produced with this .. |
|||
Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi | Calculated from mfr's report of 182 N/cm per ASTM D828 and the typical thickness |
DuPont™ Nomex® 414 Paper, 15 mil Nominal Thickness Nomex® Type 414 is designed for uses requiring a strong, yet flexible and conformable sheet. It is electrically and thermally similar to Type 410. Type 414 was designed as slot insulation in hand.. |
|||
Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi | ASTM D882 |
Dow FLEXOMER™ ETS-9064 NT 7, 2mil Very Low Density Polyethylene (VLDPE) Resin FLEXOMER™ ETS-9064 NT 7 is intended for use in single of multi-layer blown-film constructions or thick sheets. Films extruded from ETS-9064 NT 7 have a high tear strength, high impact strength, an.. |
|||
Film Tensile Strength at Break, TD | 44.8 MPa | 6500 psi | |
Dow Primacor® 1410 Ethylene Acrylic Acid (EAA) Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical. |