- Polymer Property : Flexural Yield Strength = 25400 psi
Polymer Property : Flexural Yield Strength = 25400 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical Resistant |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical Resistant |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics EXTEM UH1006M TPI Blend High heat amorphous TPI Blend, Chemical Resistant |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics EXTEM UH1006M TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical Resistant |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical Resistant, High Flow |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Extem UH1016M TPI Blend High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Extem UH1016M TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Extem UH1016M TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics EXTEM UH1026 TPI Blend High heat amorphous TPI Blend, Chemical Resistant, High Flow, IR-Transparent |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | ASTM D790-70 |
| Budd DSM-971 Smooth Surface, Class "A" SMC
(discontinued **) Parts requiring high strength and dimensional stability, excellent surface smoothness without sink marks; parts to be painted requiring an automotive-type finish.Data provided by the manufacturer. |
|||
| Flexural Yield Strength | 175 - 840 MPa | 25400 - 122000 psi | Average value: 310 MPa Grade Count:127 |
| Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E.. |
|||
| Flexural Yield Strength | 175 - 455.054 MPa @Temperature -40.0 - 149 °C |
25400 - 66000.1 psi @Temperature -40.0 - 300 °F |
Average value: 264 MPa Grade Count:6 |
| Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | ISO 178 |
| Solvay Technyl® A 218 V30 Nylon 66, 30% Glass Fiber, EH50 Polyamide PA66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V30 is used in all sectors of industry, offering an excellent combination between thermal and.. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® ENH4550 PBT (Asia Pacific) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® ENH4560 PBT (Asia Pacific) Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® IQNH4560 PBT (Asia Pacific) Valox* IQNH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP OF006 PPS - Linear LNP* THERMOCOMP* OF006 is a compound based on Linear PPS containing 30% Glass Fiber. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP VERTON MV008 PP (Europe-Africa-Middle East) LNP* VERTON* MV008 is a compound based on Polypropylene resin containing Long Glass. Added features include Chemically Coupled. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GFN1630V PPE+HIPS Noryl* GFN1630V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid en.. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GFN1630V PPE+HIPS (Asia Pacific) Noryl* GFN1630V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid en.. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DE003M PC LNP* STAT-KON* DE003M is a compound based on Polycarbonate containing 15% Milled Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GFN1630V PPE+HIPS (Europe-Africa-Middle East) Noryl* GFN1630V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid en.. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | ASTM D790 |
| Tipco Tipcofil® AG 300 - 15% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability 15% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | ISO 178 |
| Wellman Wellamid® GF13-66 22LH-N 13% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data .. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | ISO 178 |
| Wellman Wellamid® GF13-66 XE-N 13% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data .. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | ASTM D790 |
| Chem Polymer Chemlon 115 G Nylon 66, 15% Glass Fiber Reinforced A 15% glass fiber reinforced nylon 66 offering improved creep resistance, stiffness, tensile strength and dimensional stability over unmodified nylon 66 materials. This product offers slight improv.. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | ASTM Data |
| BASF Capron® HPN 9315G Impact Modified, 15% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9315G is a 15% glass reinforced, impact modified polyamide 6 injection molding grade resin in the High Productivity Nylon Series developed for applications requiring superior dry-as-molde.. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | ASTM D790 |
| Solvay Specialty Polymers Ixef® 2530/X9027 Polyarylamide, 55% Mineral + Glass Fiber, at Equilibrium (65% RH)
The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A.. |
|||
| Flexural Yield Strength | 175 MPa | 25400 psi | ASTM D790 |
| E-Polymers TEKAMID® TB120GM40 , 40% GF/MF Reinforced PA6, DAM 40% GF/MF reinforced, Good surface, Low warpageInformation provided by E-Polymers Co. Ltd. |
|||