Polymer Property : Flexural Yield Strength = 30000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	207 MPa	30000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFP36XXZ PA 66 (Asia Pacific) LNP Lubricomp RFP36XXZ is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: internally lubricated. Also known as Lubricomp RFL-4536 ..
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
Techmer ES ElectrafilÂ® J-1/CF/10 Nylon 66, 10% Carbon Fiber Reinforced
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
Techmer ES ElectrafilÂ® J-3/CF/10 Nylon 6, 10% Carbon Fiber Reinforced
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
Techmer ES ElectrafilÂ® J-50/CF/20/TF/15 Polycarbonate, 20% Carbon Fiber Reinforced, 15% PTFE
Flexural Yield Strength	207 MPa	30000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DX10313 PC (Asia Pacific) DX10313 is high modulus polycarbonate, 50% glass filled, with balanced flow and impact strength
Flexural Yield Strength	207 MPa	30000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Europe-Africa-Middle East) 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Afr..
Flexural Yield Strength	207 MPa	30000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP 9X94104 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* 9X94104 is a compound based on Polyetherimide resin containing Glass Fiber.
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
Techmer ES HiFillÂ® PPS/F GF10 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by WeightAppearance: Natural ColorInformation provided by TP Composites, Inc.
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
Techmer ES HiFillÂ® TPX-HTN-01033 A 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Heat StabilizerFeatures: Heat Stabilized and High Temperature StrengthUL File ..
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
Techmer ES HiFillÂ® TPX-HTN-03003 A 40% Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 40% Filler by WeightFeatures: Platable and High Temperature StrengthUL File Number: E157318Information provided by TP C..
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
Clariant Renol BR2065 Nylon 66, Mineral/Glass Reinforced Data provided by Clariant Masterbatches
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
Clariant Renol PA211N40 Nylon 6, Mineral/Glass Fiber, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
A. Schulman ComAlloy E-17099B Nylon 6/6, Electrically Conductive - Carbon Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Yield Strength	207 MPa	30000 psi	ASTM D790
PolyOne Stat-Tech™ RA-06CF-09GF/000 EM Polyarylsulfone - ESD Applications - Flow Enhanced Grade (discontinued Data provided by PolyOne.
Flexural Yield Strength	207 MPa	30000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem ATX103R PEI+PCE 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Americas r..
Flexural Yield Strength	207 MPa	30000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Asia Pacific) 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Asia Pacif..