Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 739 MPa @Temperature 25.0 °C |
107000 psi @Temperature 77.0 °F |
|
Haynes HR-224® Nickel Alloy Alloy with excellent oxidation resistance and improved fabricability and weldability compared to HAYNES® 214® alloy. This Ni–27.5Fe–20Cr–3.8Al alloy achieves superior oxidation .. |
|||
Tensile Strength, Ultimate | 740 MPa @Diameter 12.7 mm, Temperature 25.0 °C |
107000 psi @Diameter 0.500 in, Temperature 77.0 °F |
|
Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
Tensile Strength, Ultimate | 738 MPa @Temperature 21.1 °C |
107000 psi @Temperature 70.0 °F |
Plate |
Special Metals INCOLOY® 25-6HN Super-Austenitic Stainless Steel INCOLOY alloy 25-6HN is a super-austenitic stainless steel containing 6% molybdenum and with properties enhanced by its content of nitrogen. Its high content of nickel results in thermal stability .. |
|||
Tensile Strength, Ultimate | 738 MPa @Diameter 88.9 mm, Temperature 25.0 °C |
107000 psi @Diameter 3.50 in, Temperature 77.0 °F |
|
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
Tensile Strength, Ultimate | 738 MPa @Diameter 19.1 mm, Temperature 25.0 °C |
107000 psi @Diameter 0.752 in, Temperature 77.0 °F |
|
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |