Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	765 MPa @Thickness 3.17 mm	111000 psi @Thickness 0.125 in
Haynes HastelloyÂ® C-2000Â® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate	767 MPa @Temperature 100 Â°C	111000 psi @Temperature 212 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	765 MPa @Thickness 12.7 mm, Temperature 93.0 Â°C	111000 psi @Thickness 0.500 in, Temperature 199 Â°F
Haynes HastelloyÂ® C-4 alloy, plate, heat treated at 1066Â°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Tensile Strength, Ultimate	767 MPa @Thickness 6.30 mm, Temperature 20.0 Â°C	111000 psi @Thickness 0.248 in, Temperature 68.0 Â°F
Haynes HastelloyÂ® C-4 alloy, plate, heat treated at 1066Â°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Tensile Strength, Ultimate	763 MPa @Thickness 3.20 mm, Temperature 204 Â°C	111000 psi @Thickness 0.126 in, Temperature 399 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	764 MPa @Diameter 12.7 mm, Temperature 25.0 Â°C	111000 psi @Diameter 0.500 in, Temperature 77.0 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	765 MPa @Thickness 6.35 mm, Temperature 20.0 °C	111000 psi @Thickness 0.250 in, Temperature 68.0 °F
Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Tensile Strength, Ultimate	768 MPa @Thickness 1.70 mm, Temperature 20.0 °C	111000 psi @Thickness 0.0669 in, Temperature 68.0 °F
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..