Polymer Property : Tensile Strength, Ultimate = 117000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	809 MPa @Temperature 315 Â°C	117000 psi @Temperature 599 Â°F	AMS 5879
Haynes 625SQÂ® Nickel Alloy Sheet Haynes 625SQ alloy is a solid-solution strengthened superalloy. It is a modification of Haynes 625 alloy designed to enhance resistance to fatigue at temperatures up to approximately 1200Â°F (649Â..
Tensile Strength, Ultimate	806 MPa @Temperature 25.0 Â°C	117000 psi @Temperature 77.0 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	807 MPa @Temperature 100 Â°C	117000 psi @Temperature 212 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	805 MPa @Thickness 12.7 mm, Temperature 20.0 Â°C	117000 psi @Thickness 0.500 in, Temperature 68.0 Â°F
Haynes HastelloyÂ® C-4 alloy, plate, heat treated at 1066Â°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Tensile Strength, Ultimate	809 MPa @Thickness 19.1 mm, Temperature 25.0 °C	117000 psi @Thickness 0.752 in, Temperature 77.0 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..