Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 980 MPa @Temperature 600 °C |
142000 psi @Temperature 1110 °F |
|
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Tensile Strength, Ultimate | 977 MPa @Thickness 12.7 mm, Temperature 25.0 °C |
142000 psi @Thickness 0.500 in, Temperature 77.0 °F |
As Welded and Solution Annealed at 2075°F(1135°C)/30min/AC, Base/Base Fracture |
Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Tensile Strength, Ultimate | 980 - 1320 MPa @Diameter 11.0 mm |
142000 - 191000 psi @Diameter 0.433 in |
Rm. Core strength in hardened condition. |
Assab Steels 7210M Machinery Steel ASSAB 7210M is an alloyed case hardening steel with high core strength.Applications: ASSAB 7210M is used for applications requiring a hard, wear resistant surface and a tough core, such as transmiss.. |