Polymer Property : Tensile Strength, Ultimate = 149000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1030 MPa @Temperature 650 Â°C	149000 psi @Temperature 1200 Â°F	Precipitation Hardened prior to test
Special Metals INCONELÂ® Alloy 751 A nickel-chromium alloy similar to INCONEL ALLOY X-750 but with increased aluminum content for greater precipitation hardening. INCONEL alloy 751 was designed for use as exhaust valves in internal-..
Tensile Strength, Ultimate	1030 MPa @Temperature 650 Â°C	149000 psi @Temperature 1200 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 105 A precipitation-hardenable nickel-cobalt-chromium alloy with an addition of molybdenum for solid-solution strengthening. The relatively high aluminum content enhances both strength (through greater..
Tensile Strength, Ultimate	1030 MPa @Temperature 650 Â°C	149000 psi @Temperature 1200 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 80A A nickel-chromium alloy similar to NIMONIC alloy 75 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good corrosion and oxidation resistance and high tensile a..
Tensile Strength, Ultimate	1030 MPa @Temperature 550 Â°C	149000 psi @Temperature 1020 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 90 A precipitation-hardenable nickel-chromium-cobalt alloy having high stress-rupture strength and creep resistance at temperatures to about 1700Â°F (920Â°C). The alloy also has good resistance to..
Tensile Strength, Ultimate	1030 MPa @Temperature 550 Â°C	149000 psi @Temperature 1020 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 901 A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at ..