Polymer Property : Tensile Strength, Ultimate = 160000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1100 MPa @Temperature 400 Â°C	160000 psi @Temperature 752 Â°F
International Mold Steel DH2F Pre-Hardened H13-Type Mold Steel Description: DH2F is one of the best machining pre-hardened H13-type steels available.Unique Characteristics: 38-42 HRc hardness.Through hardened for exceptional dimensional stability.Cuts mold maki..
Tensile Strength, Ultimate	1103 MPa @Temperature 300 Â°C	160000 psi @Temperature 572 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	1100 MPa @Temperature 650 Â°C	160000 psi @Temperature 1200 Â°F	Precipitation Hardened prior to test
Special Metals INCONELÂ® Alloy 718 Developed in the early 1960's, IN718 is still considered the material of choice for the majority of aircraft engine components with service temperatures below 1200Â°F (650Â°C). Inconel 718 is a..
Tensile Strength, Ultimate	1100 MPa @Temperature 23.0 Â°C	160000 psi @Temperature 73.4 Â°F
Special Metals MONELÂ® Alloy K-500 A precipitation-hardenable nickel-copper alloy that combines the corrosion resistance of MONEL alloy 400 with greater strength and hardness. It also has low permeability and is nonmagnetic to under..
Tensile Strength, Ultimate	1100 - 1380 MPa @Temperature 315 °C	160000 - 200000 psi @Temperature 599 °F	varies with heat treatment
Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel A premium grade H13 hot work tool steel featuring:Very good toughness properties meeting the requirements of NADCA 207-97, and the superior quality levels of NADCA 207-2003Very good heat checking re..
Tensile Strength, Ultimate	1100 - 1380 MPa @Temperature 315 °C	160000 - 200000 psi @Temperature 599 °F	varies with heat treatment
Bohler-Uddeholm BÖHLER W303 ISODISC® Hot Work Tool Steel Description: Hot work tool steel featuring excellent hot tensile properties, high retention of hardness, good toughness and resistance to heat checking, admits water cooling. BOHLER W303 is also ava..
Tensile Strength, Ultimate	1100 - 1380 MPa @Temperature 315 °C	160000 - 200000 psi @Temperature 599 °F	varies with heat treatment
Bohler-Uddeholm BÖHLER W302 ISOBLOC® H13 hot work tool steel Properties:Hot work tool steel featuring excellent hot tensile properties, high hot wear resistance, adequate toughness and heat checking resistance, adequate toughness and heat checking; admits wat..