Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 1160 MPa @Thickness 3.20 mm, Temperature 25.0 °C |
168000 psi @Thickness 0.126 in, Temperature 77.0 °F |
As Welded and Aged at 1850°F(1010°C)/2hr/AC + 1450°F(788°C)/8h/AC; Base/Weld Fracture |
Haynes 282® Nickel Alloy Autogenously Welded Sheet Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Tensile Strength, Ultimate | 1160 MPa @Temperature 550 °C |
168000 psi @Temperature 1020 °F |
Precipitation Hardened prior to test |
Special Metals INCOLOY® Alloy 909 A nickel-iron-cobalt alloy with a silicon addition and containing niobium and titanium for precipitation hardening. It is similar to INCOLOY alloys 903 and 907 in that it has low thermal expansion .. |