Polymer Property : Tensile Strength, Ultimate = 656 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	656 MPa @Temperature 149 Â°C	95100 psi @Temperature 300 Â°F
Haynes HastelloyÂ® G-35Â® Nickel Alloy Plate, Annealed at 2075Â°F (1135Â°C) Known for its corrosion performance, HASTELLOYÂ® G-35Â® alloy was designed to resist â€œwet processâ€ phosphoric acid, which is widely used in the production of fertilizers. Tests indicat..
Tensile Strength, Ultimate	656 MPa @Thickness 1.70 mm, Temperature 427 °C	95100 psi @Thickness 0.0669 in, Temperature 801 °F
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Tensile Strength, Ultimate	656 MPa @Thickness 4.00 mm, Temperature 427 °C	95100 psi @Thickness 0.157 in, Temperature 801 °F
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Tensile Strength, Ultimate	656 MPa @Temperature 149 °C	95100 psi @Temperature 300 °F
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is..