Polymer Property : Tensile Strength = 39200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	270 MPa @Diameter 20.0 - 40.0 mm	39200 psi @Diameter 0.787 - 1.57 in
United Cast Bar Unibar 300 Continuously Cast Iron Unibar 300 is alloyed to achieve the properties, giving excellent wear resistance, strength & heat-treatment response, while still possessing reasonable machinability and an excellent surface finish..
Tensile Strength	>= 270 MPa @Thickness 6.30 - 12.5 mm	>= 39200 psi @Thickness 0.248 - 0.492 in	Temper H111; Standard EN 485-2
Constellium PLAN 5083 Aluminum Rolled Plate Rolled plates in 5083 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 5083 PLAN is mainly used for low stressed mechanical components, manufactured by intensive m..
Tensile Strength	>= 270 MPa @Thickness 12.5 - 50.0 mm	>= 39200 psi @Thickness 0.492 - 1.97 in	Temper H111; Standard EN 485-2
Constellium PLAN 5083 Aluminum Rolled Plate Rolled plates in 5083 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 5083 PLAN is mainly used for low stressed mechanical components, manufactured by intensive m..
Tensile Strength	>= 270 MPa @Thickness 50.0 - 80.0 mm	>= 39200 psi @Thickness 1.97 - 3.15 in	Temper H111; Standard EN 485-2
Constellium PLAN 5083 Aluminum Rolled Plate Rolled plates in 5083 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 5083 PLAN is mainly used for low stressed mechanical components, manufactured by intensive m..
Tensile Strength	>= 270 MPa @Thickness 8.00 - 12.5 mm	>= 39200 psi @Thickness 0.315 - 0.492 in	Tempers O/H111; Standard EN 485-2
Constellium Planoxal® 50 Aluminum plate Planoxal®-50 plates differ from other standard EN-AW 5083 alloy products by their low level of residual stress. This specialty plate is also suitable for decorative anodizing. Planoxal®-50 is main..
Tensile Strength	>= 270 MPa @Thickness 12.5 - 50.0 mm	>= 39200 psi @Thickness 0.492 - 1.97 in	Tempers O/H111; Standard EN 485-2
Constellium Planoxal® 50 Aluminum plate Planoxal®-50 plates differ from other standard EN-AW 5083 alloy products by their low level of residual stress. This specialty plate is also suitable for decorative anodizing. Planoxal®-50 is main..
Tensile Strength	>= 270 MPa @Thickness 50.0 - 80.0 mm	>= 39200 psi @Thickness 1.97 - 3.15 in	Tempers O/H111; Standard EN 485-2
Constellium Planoxal® 50 Aluminum plate Planoxal®-50 plates differ from other standard EN-AW 5083 alloy products by their low level of residual stress. This specialty plate is also suitable for decorative anodizing. Planoxal®-50 is main..
Tensile Strength	>= 270 MPa @Thickness 6.00 - 12.5 mm	>= 39200 psi @Thickness 0.236 - 0.492 in	Temper H111; Standard EN 485-2
Constellium ALPLAN® 5083 Rolled Precision Aluminum Plate, Milled Both Sides ALPLAN® 5083 precision plates exhibit good dimensional stability. Their low internal stresses reduces the effects of plate deformation during machining, thus saving on extra operations such as roug..
Tensile Strength	>= 270 MPa @Thickness 12.5 - 50.0 mm	>= 39200 psi @Thickness 0.492 - 1.97 in	Temper H111; Standard EN 485-2
Constellium ALPLAN® 5083 Rolled Precision Aluminum Plate, Milled Both Sides ALPLAN® 5083 precision plates exhibit good dimensional stability. Their low internal stresses reduces the effects of plate deformation during machining, thus saving on extra operations such as roug..
Tensile Strength	>= 270 MPa @Thickness 50.0 - 80.0 mm	>= 39200 psi @Thickness 1.97 - 3.15 in	Temper H111; Standard EN 485-2
Constellium ALPLAN® 5083 Rolled Precision Aluminum Plate, Milled Both Sides ALPLAN® 5083 precision plates exhibit good dimensional stability. Their low internal stresses reduces the effects of plate deformation during machining, thus saving on extra operations such as roug..