Polymer Property : Tensile Strength, Ultimate = 139000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	958 MPa	139000 psi
Kennametal Stellite NucalloyÂ® 453 High-Silicon Nickel-Base Hardfacing Alloy Applications include chemical control valves, nuclear globe valves, nuclear gate valves, nuclear sliding parts, and pressure bars for plywood cutters.NucalloyÂ® alloys are unique, patented, high-s..
Tensile Strength, Ultimate	960 - 1140 MPa	139000 - 165000 psi
Materion Beryllium Copper Alloy 25 Wire; H (TD04) Temper; 1.3-2.0 mm Diameter (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to..
Tensile Strength, Ultimate	>= 960 MPa	>= 139000 psi
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM04 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 98%Stress Relaxation after 1000 hrs @ 200Â°C: 77%Formability Ratio, 90Â° Bend, R..
Tensile Strength, Ultimate	961 MPa	139000 psi	at Center, Transverse
International Mold Steel PX5 Pre-Hardened Mold Steel (P20 Type) PX5 is a modified P20, high performance, high precision, mold steel. Unique Characteristics: Exceptionally clean steel with uniform microstructure â€“ no pin holes, inclusions or hard spots. 30-3..
Tensile Strength, Ultimate	961 MPa	139000 psi	at Center, Longitudinal
International Mold Steel PX5 Pre-Hardened Mold Steel (P20 Type) PX5 is a modified P20, high performance, high precision, mold steel. Unique Characteristics: Exceptionally clean steel with uniform microstructure â€“ no pin holes, inclusions or hard spots. 30-3..
Tensile Strength, Ultimate	960 MPa	139000 psi
Haynes 214Â® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	960 MPa	139000 psi
Haynes 230Â® alloy, 10% cold reduction, 1121Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate	960 MPa	139000 psi
Haynes 230Â® alloy, 40% cold reduction, 1177Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate	958 MPa @Temperature 538 Â°C	139000 psi @Temperature 1000 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Tensile Strength, Ultimate	958 MPa	139000 psi
Haynes UltimetÂ® alloy, aged 1000 hours at 871Â°C (1600Â°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	960 - 1140 MPa	139000 - 165000 psi
Materion Beryllium Copper Alloy M25 Wire; H (TD04) Temper; 1.3-2.0 mm Diameter (UNS C17300) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to..
Tensile Strength, Ultimate	958 MPa @Thickness 50.8 mm, Temperature 371 Â°C	139000 psi @Thickness 2.00 in, Temperature 700 Â°F
Latrobe LescalloyÂ® 6305 VAC-ARC ; High Strength Alloy Steel LESCALLOY 6305 VAC-ARC steel is a modified 4140 steel with higher molybdenum and a vanadium addition. The alloy steel is generally used in the 160/180,000 psi tensile strength range obtained with a..
Tensile Strength, Ultimate	959 MPa @Temperature 23.0 °C	139000 psi @Temperature 73.4 °F
Crucible Compaction Metals P/M N625 Corrosion Resistant Alloy P/M N625 (chemically, UNS N06625) is produced by the state-of-the-art Crucible P/M process: inert gas atomization, coupled with consolidation by hot isostatic pressing (HIP) and/or extrusion. The a..