Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	834 MPa @Temperature 600 Â°C	121000 psi @Temperature 1110 Â°F
Kennametal Stellite NucalloyÂ® 488V High-Silicon Nickel-Base Hardfacing Alloy Applications include diesel engine valves, and injection mold screws.NucalloyÂ® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinati..
Tensile Strength, Ultimate	835 MPa @Temperature 650 Â°C	121000 psi @Temperature 1200 Â°F
Haynes 263Â® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle..
Tensile Strength, Ultimate	834 MPa @Thickness 3.20 mm	121000 psi @Thickness 0.126 in	Sheet
Haynes 282Â® Nickel Alloy Sheet, Plate and Bar, Solution Annealed Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Ultimate	835 MPa	121000 psi
Haynes 556Â® alloy, bar, after 4000 hours at 650Â°C (1200Â°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	>= 834 MPa	>= 121000 psi
Crucible Steel JIS SUH600 Martensitic Steel Information provided by Crucible Specialty Metals.
Tensile Strength, Ultimate	834 MPa @Temperature 427 °C	121000 psi @Temperature 801 °F
Carpenter Custom 450® Stainless Steel, Condition H1050 (Age Hardened 566°C) Data provided by Carpenter Technology Corporation.Custom 450® stainless is a martensitic age-hardenable stainless steel which exhibits very good corrosion resistance (similar to that of Stainless T..