Polymer Property : Tensile Strength, Ultimate = 165000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	>= 1140 MPa	>= 165000 psi	Annealed and Aged
IBC Advanced Alloys FA230 Beryllium Nickel Casting Alloy Beryllium nickel casting alloys are characterized by their steel-like high strength, toughness, and hardness properties. However, unlike the steel alloys, the beryllium nickel alloy system offers th..
Tensile Strength, Ultimate	1140 - 1250 MPa	165000 - 181000 psi	Solution Annealed & Aged
Materion Beryllium Copper Alloy 245C Castings (UNS C82600) Pouring Temperature: 970-1065Â°CHeat treatment required for max strength (Annealing): 760-790Â°C/water quenchHeat treatment required for max strength (Hardening): 760-790Â°C/water quenchTabula..
Tensile Strength, Ultimate	1140 MPa @Temperature 315 Â°C	165000 psi @Temperature 599 Â°F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595Â°C (1100Â°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	1140 - 1250 MPa	165000 - 181000 psi	Solution Annealed & Aged
Materion Beryllium Copper Alloy 245CT Castings (UNS C82600) Pouring Temperature: 970-1065Â°CHeat treatment required for max strength (Annealing): 760-790Â°C/water quenchHeat treatment required for max strength (Hardening): 760-790Â°C/water quenchTabula..
Tensile Strength, Ultimate	1140 MPa	165000 psi
Haynes 25 alloy, room temperature after 25% cold reduction, 1120Â°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	1140 MPa	165000 psi
Haynes 625 alloy, plate after 1000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate	1140 MPa	165000 psi
Haynes 625 alloy, plate after 16000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate	1140 MPa	165000 psi	593Â°C Temper Temperature
Latrobe LescalloyÂ® 4340 VAC-ARC ; 10.5" square High Strength Alloy Steel LESCALLOY 4340 VAC-ARC steel is a low alloy, nickel-chromium-molybdenum steel capable of being heat treated to high strength levels. The alloy has a good combination of ductility, toughness and str..
Tensile Strength, Ultimate	1140 MPa	165000 psi	Age Hardened
Universal Wire Works Inconel 718 (AMS 5832) Filler Metal Inconel Filler Metal 718 is recommended for gas tungsten arc and gas metal arc welding of alloy 718, 706 and X-750. This double gamma prime alloy has excellent strength, good ductility up to 1300°F..
Tensile Strength, Ultimate	1140 MPa	165000 psi	(hardened to 350 HB)
Bohler-Uddeholm BÖHLER RAMAX® HH Modified 420F Chromium alloyed steelTypical applications for Ramax® HH are: holders and bolsters for plastic molds, plastic and rubber molds with low requirements on polishability, and dies for plastic extrusion..