Polymer Property : Tensile Strength, Ultimate = 700 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	700 MPa	102000 psi	Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Outokumpu 253MA® High Temperature Austenitic Stainless Steel Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used be..
Tensile Strength, Ultimate	700 MPa	102000 psi
Kennametal Stellite TribaloyÂ® T-800 Applications: Used in applications with high temperatures and severe wear, abrasion, and corrosion.Weldability: Can be PTA welded with a preheat of 538Â°C (1000Â°F) or higher.Wear: Wear test ..
Tensile Strength, Ultimate	>= 700 MPa	>= 102000 psi
SSAB Tunnplat DomexÂ® 640XP Extra High-strength Cold-forming Steel Extra High-strength Cold-forming Steel, HSLACharacteristics: DomexÂ® is the brand name of hot rolled products from SSAB Tunnplat. DomexÂ® cold-forming steels are modern structural steels. Gene..
Tensile Strength, Ultimate	700 - 880 MPa	102000 - 128000 psi
SSAB Tunnplat DomexÂ® 650MC HSLA Steel HSLA SteelCharacteristics: DomexÂ® MC grade steels conform to the provisions of EN 10149-2 standard and often have better properties.Property data is for hot-rolled steel..DomexÂ® is the brand n..
Tensile Strength, Ultimate	700 - 800 MPa	102000 - 116000 psi	Wire
CLAL-MSX ARCAP Anticorrosion AP1C H13 3/4 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un..
Tensile Strength, Ultimate	700 - 800 MPa	102000 - 116000 psi
CLAL-MSX NICLAFOR® 1000 TD3 Quenched/Cold Rolled, Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Ultimate	700 - 820 MPa	102000 - 119000 psi
CLAL-MSX NICLAFOR® 1000 TD4 Quenched/Cold Rolled, Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Ultimate	>= 700 MPa	>= 102000 psi	Rod
CLAL-MSX ARCAP Anticorrosion AP1C H15 Spring, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un..
Tensile Strength, Ultimate	700 - 800 MPa	102000 - 116000 psi
CLAL-MSX DECLAFOR® 1015 TF Wire quenched/Precipitation Heat Treated Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn..
Tensile Strength, Ultimate	700 MPa	102000 psi	Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Outokumpu LDX 2101® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone..