Polymer Property : Tensile Strength, Ultimate = 705 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	705 MPa @Temperature 760 Â°C	102000 psi @Temperature 1400 Â°F
Haynes 214Â® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	705 MPa	102000 psi
Haynes HastelloyÂ® S alloy, weld metal, aged at 649Â°C (1200Â°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	705 MPa @Temperature 425 Â°C	102000 psi @Temperature 797 Â°F
Haynes HastelloyÂ® B-3Â® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Ultimate	705 MPa @Temperature 538 °C	102000 psi @Temperature 1000 °F
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..