Polymer Property : Tensile Strength, Ultimate = 790 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	790 - 940 MPa	115000 - 136000 psi	Guaranteed, 1/4 t
Industeel SUPERELSOÂ® 690CR Quenched and Tempered High Strength Steel for Leg Components of Jack-up Rigs SuperelsoÂ® 690 CR (SE 690 CR) is a 690MPa (100ksi) yield strength quenched and tempered steel adapted for jack-up rig legs of offshore drilling platforms. SuperelsoÂ® 690 CR is manufactured via..
Tensile Strength, Ultimate	790 MPa @Temperature 650 Â°C	115000 psi @Temperature 1200 Â°F
Haynes 214Â® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	790 - 930 MPa	115000 - 135000 psi
Materion Brush 60â„¢ 3/4 HT Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 96%Stress Relaxation afte..
Tensile Strength, Ultimate	>= 790 MPa	>= 115000 psi
MetalTek INÂ® 100 UNS N13100 Centri-Vac Nickel Based Alloy Information provided by MetalTek
Tensile Strength, Ultimate	790 MPa	115000 psi
Haynes 556Â® alloy, 0% cold reduction, 1010Â°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	790 MPa	115000 psi	Annealed
Special Metals INCONELÂ® Alloy C-276 A nickel-molybdenum-chromium alloy with an addition of tungsten having excellent corrosion resistance in a wide range of severe environments. The high molybdenum content makes the alloy especially ..
Tensile Strength, Ultimate	>= 790 MPa	>= 115000 psi
SSAB Tunnplat DomexÂ® 740XP Extra High-strength Cold-forming Steel Extra High-strength Cold-forming Steel, HSLACharacteristics: DomexÂ® is the brand name of hot rolled products from SSAB Tunnplat. DomexÂ® cold-forming steels are modern structural steels. Gene..
Tensile Strength, Ultimate	790 MPa	115000 psi	Typical
ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, Annealed at 982°C (1800°F), UNS N06601 Allegheny Ludlum's AL 601 alloy is an austenitic nickel-chromium-iron alloy designed for both heat and corrosion resistance. As compared to AL 600 alloy, the AL 601 alloy has, in addition to increa..