Polymer Property : Tensile Strength, Ultimate = 952 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	952 MPa @Temperature 760 Â°C	138000 psi @Temperature 1400 Â°F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Tensile Strength, Ultimate	952 MPa	138000 psi
Haynes UltimetÂ® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	952 MPa @Temperature 316 Â°C	138000 psi @Temperature 601 Â°F
Haynes UltimetÂ® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	952 MPa	138000 psi
Haynes UltimetÂ® alloy, aged 1000 hours at 760Â°C (1400Â°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	952 MPa @Temperature 482 °C	138000 psi @Temperature 900 °F
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 900 (Age-Hardened 482°C/1hr/AC) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio..