Polymer Property : Tensile Strength, Ultimate = 980 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	980 MPa	142000 psi
Haynes 230Â® alloy, 20% cold reduction, 1066Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate	980 MPa	142000 psi
Haynes 230Â® alloy, 30% cold reduction, 1066Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate	980 MPa	142000 psi
Haynes 230Â® alloy, 40% cold reduction, 1121Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate	980 MPa	142000 psi
Haynes 25 alloy, room temperature sheet after 1000 hours of 870Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	980 - 1100 MPa	142000 - 160000 psi
ArcelorMittal Dual Phase 980 LCE Y660 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft ..
Tensile Strength, Ultimate	980 - 1200 MPa	142000 - 174000 psi
ArcelorMittal Complex Phase Steel 1000 SF Very high strength steel, Cold Rolled Steel Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product range. These steels are cold formed to make lightweight structural elements. A num..
Tensile Strength, Ultimate	980 - 1200 MPa	142000 - 174000 psi
ArcelorMittal Complex Phase Steel 1000 Very high strength steel, Cold Rolled Steel Available in the following: uncoated (HCT980C) and electrogalvanized (HCT980C+ZE)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product r..
Tensile Strength, Ultimate	980 - 1130 MPa	142000 - 164000 psi
ArcelorMittal Complex Phase Steel 1000 Y800 Very high strength steel, Cold Rolled Steel Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product range. These steels are cold formed to make lightweight structural elements. A num..
Tensile Strength, Ultimate	980 - 1100 MPa	142000 - 160000 psi
ArcelorMittal Dual Phase 1180 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft ..
Tensile Strength, Ultimate	980 - 1100 MPa	142000 - 160000 psi
ArcelorMittal Dual Phase 980 LCE Y700 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft ..
Tensile Strength, Ultimate	980 - 1100 MPa	142000 - 160000 psi
ArcelorMittal Dual Phase 980 Y700 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft ..
Tensile Strength, Ultimate	980 MPa	142000 psi
Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..