Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 0.800 MPa | 116 psi | Typical; ASTM C273 |
Parabeam Industrie Paraglass 5 3D Glass Fabric Parabeam® 3D Glass Fabric is a fabric woven out of a 100% E-glass yarn and consists of two decklay one-step process a lightweight and strong sandwich laminate is formed that offers excellent mechan.. |
|||
Shear Strength | 0.800 MPa | 116 psi | ASTM C273 |
SABIC Innovative Plastics ULTEM Foam XP060 PEI ULTEM foam is a polyetherimide based thermoplastic foam with excellent flame, smoke and toxicity performance. The material combines a high strength to weight ratio with low moisture absorption. The .. |
|||
Shear Strength | 0.800 MPa | 116 psi | Plate Shear, L direction |
Hexcel® HexWeb® CRF-3/8-ACG-.002-2.3 Chromate free ACG® Honeycomb Hexweb CRF is a hexagonal cell aluminum honeycomb material used principally as a shear carrying core in light weight adhesively bonded sandwich structures, and suitable for a wide range of other app.. |
|||
Shear Strength | >= 0.800 MPa | >= 116 psi | ISO 1922 |
3A Composites Core Materials AIREX® R63.80 Damage Tolerant Foam AIREX® R63 is a closed-cell, linear, thermoplastic polymer foam with extremely high damage tolerance. This formula combines high elongation and excellent bond strength. AIREX® R63 is cold formable.. |
|||
Shear Strength | 0.800 MPa | 116 psi | average; ISO 1922 |
3A Composites Core Materials AIREX® R82.60 High Performance Structural Foam AIREX® R82 is a closed-cell, thermoplastic polymer foam that combines fire resistance with low smoke and toxicity, along with good dielectric properties. It has a good strength to weight ratio, ver.. |
|||
Shear Strength | 0.800 MPa | 116 psi | average; ISO 1922 |
3A Composites Core Materials AIREX® T90.100 Easy Processing Structural FST Foam AIREX® T90 is a closed-cell, thermoplastic and recyclable polymer foam with excellent fire, smoke & toxicity (FST) properties. It has very good mechanical properties and a good resistance to fatigu.. |
|||
Shear Strength | 0.800 - 128 MPa | 116 - 18600 psi | Average value: 78.5 MPa Grade Count:18 |
Overview of materials for Polyetherimide (PEI) This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide". Each property range of values reported is minimum and maximum values of appropriate Mat.. |