Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | >= 2.48 MPa | >= 360 psi | Plate Shear, W Direction, min, preliminary value obtained from limited testing |
Hexcel® HexWeb® CFC™-20-1/8-11.0 Composite Flooring Honeycomb Core Hexweb CFC™-20 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes and, after expanding to the hexagonal confiation, the block is dipp.. |
|||
Shear Strength | >= 2.48 MPa | >= 360 psi | Plate Shear, W Direction, min |
Hexcel® HexWeb® CR III 5/32-5056-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | >= 2.48 MPa | >= 360 psi | Plate Shear, W Direction, min |
Hexcel® HexWeb® CR-PAA™ 5/32-5056-0.002 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
Shear Strength | 2.48 MPa @Time 1.80e+6 sec |
359 psi @Time 500 hour |
Overlap, Gelcoat, 50% RH, Salt Water Immersion |
3M 4000 UV 5280 Marine Adhesive/Sealant Fast Cure 3M™ Marine Adhesive/Sealant 4000 UV is a one-part adhesive sealant that cures to form a firm, rubbery waterproof seal. Its flexibility allows for the dissipation of stress caused by shock, vibratio.. |
|||
Shear Strength | 2.48 MPa @Time 1.80e+6 sec |
359 psi @Time 500 hour |
Overlap, Gelcoat, 50% RH, Salt Water Immersion |
3M 4000 UV 6580 Marine Adhesive/Sealant Fast Cure 3M™ Marine Adhesive/Sealant 4000 UV is a one-part adhesive sealant that cures to form a firm, rubbery waterproof seal. Its flexibility allows for the dissipation of stress caused by shock, vibratio.. |
|||
Shear Strength | 2.48 MPa @Time 1.80e+6 sec |
359 psi @Time 500 hour |
Overlap, Gelcoat, 50% RH, Salt Water Immersion |
3M 4000 UV 6586 Marine Adhesive/Sealant Fast Cure 3M™ Marine Adhesive/Sealant 4000 UV is a one-part adhesive sealant that cures to form a firm, rubbery waterproof seal. Its flexibility allows for the dissipation of stress caused by shock, vibratio.. |
|||
Shear Strength | 2.48 MPa | 360 psi | Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, Polycarbonate |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 2.48 MPa | 360 psi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing |
Hexcel® HexWeb® CFC™-20-1/8-5.0 Composite Flooring Honeycomb Core Hexweb CFC™-20 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes and, after expanding to the hexagonal confiation, the block is dipp.. |
|||
Shear Strength | >= 2.48 MPa | >= 360 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® CR III 1/4-5052-.0025 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | >= 2.48 MPa | >= 360 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.0025 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |