Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 17.0 MPa @Temperature 982 °C, Time 3.60e+6 sec |
2470 psi @Temperature 1800 °F, Time 1000 hour |
|
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Rupture Strength | 17.0 MPa @Temperature 900 °C, Time 3.60e+7 sec |
2470 psi @Temperature 1650 °F, Time 10000 hour |
Stress Rupture |
AFE Technologies Cronite 25Cr/12Ni No. HR7 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |
|||
Rupture Strength | 17.0 MPa @Temperature 899 °C, Time 3.60e+7 sec |
2470 psi @Temperature 1650 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 309 Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 17.0 MPa @Temperature 899 °C, Time 3.60e+7 sec |
2470 psi @Temperature 1650 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 309H Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 17.0 MPa @Temperature 899 °C, Time 3.60e+7 sec |
2470 psi @Temperature 1650 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 309S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 17.0 MPa @Temperature 899 °C, Time 3.60e+7 sec |
2470 psi @Temperature 1650 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 309Si Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 17.0 MPa @Temperature 1095 °C, Time 360000 sec |
2470 psi @Temperature 2003 °F, Time 100 hour |
|
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |
|||
Rupture Strength | 17.0 MPa @Temperature 1040 °C, Time 3.60e+6 sec |
2470 psi @Temperature 1900 °F, Time 1000 hour |
|
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |
|||
Rupture Strength | 17.0 MPa @Temperature 980 °C, Time 3.60e+7 sec |
2470 psi @Temperature 1800 °F, Time 10000 hour |
|
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |