Polymer Property : Flexural Modulus = 1.80 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	1.80 GPa @Temperature 23.0 °C	261 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYblend 6005B UV PC/ABS-Blend Information provided by Polykemi AB
Flexural Modulus	1.80 - 2.10 GPa	261 - 305 ksi	ASTM D790
Prodways PLASTCure Model 200 3D Printing Polymer High temperature resistance.Thermoforming applicationsInformation provided by Genistar.
Flexural Modulus	1.80 GPa @Temperature 23.0 °C	261 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPH TS2020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics GELOY CR3020 ASA Low-gloss ASA for profile and capstock applications
Flexural Modulus	1.80 GPa	261 ksi	ISO 178, ASTM D790
Nilit Nilamid A3 H ZE High Impact PA66 Description: Nilamid A3 H ZE was developed for applications which are subjected to very high shock loads, also at minus temperatures. It has good impact performance, whilst maintaining good strength..
Flexural Modulus	1.80 GPa	261 ksi
Lehmann & Voss LUVOCOMÂ® 1850-8197 PBT, lubricant modified, easy flowing, demolding aid Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Parts for electric and electro..
Flexural Modulus	1.80 GPa	261 ksi
Lehmann & Voss LUVOCOMÂ® 50-8276 Polycarbonate, with PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts, even at elevated te..
Flexural Modulus	1.80 GPa	261 ksi
Lehmann & Voss LUVOCOMÂ® 80-7318 Polyacetal-copolymer, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl..
Flexural Modulus	1.80 - 2.00 GPa	261 - 290 ksi	ASTM D790
Loxim 830 02C HB Polypropylene Compound, 30% Calcite Filled, Flame Retardant Information provided by Loxim Industries
Flexural Modulus	1.80 GPa	261 ksi	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BC 550 Z DUSXBL 900116 Nylon 6, Impact Modified PA 6, non-reinforced, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Solvay TechnylÂ® C 206 Nylon 6, EH0 Unreinforced Plyamide PA6, standard for fast cycling, for injection molding.Technyl C 206 has high fluidity and good mold release, favored by a high crystallization rate. It is specially suitable f..
Flexural Modulus	1.80 GPa @Temperature 260 Â°C	261 ksi @Temperature 500 Â°F	ASTM D790
Saint-Gobain MeldinÂ® 7021 Direct Formed Graphite Filled Polyimide Finished parts and basic shapes made from 15% by weight graphite filled polyimide material for applications high wear resistance, good thermal oxidative stability, and high temperature resistance. ..
Flexural Modulus	1.80 GPa	262 ksi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® CA-7009 PA/PPE, Antistatic Information provided by Samsung Cheil Industries.
Flexural Modulus	1.80 GPa	261 ksi	ISO Data
Styrolution TerblendÂ® N NM-19 ABS/PA6 (Dry) Terblend N NM-19 is a UV stabilized ABS/PA6 blend combining very high impact strength, even at low temperatures with an excellent processability and surface appearance.Information provided by STYROL..
Flexural Modulus	1.80 GPa	261 ksi	ISO Data
Styrolution TerblendÂ® N NMX04 ABS/PA6 (Dry) Terblend N NMX04 is an ABS/PA6 blend specially developed for painted exterior applications, combining impact resistance with excellent processability and paintability.Information provided by STYROLU..
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min; ISO 178
Sax Polymers SAXAMID 136Q32 Nylon 6, Injection Molding Grade SAXAMID 136Q32 is a high impact-modified polyamide 6 injection-molding-grade.Information provided by SAX Polymers
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX964W PPE+PS+PA Noryl GTX* GTX964W resin is a blend of Polyphenylene Ether and Polyamide resin with very high impact and high flow. The material wsa designed for large parts, body panels, and thinwall applications..
Flexural Modulus	1.80 GPa	261 ksi	Tangent; ISO 178
A. Schulman FORMION™ FI 232 10% Mineral Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 232 is an injection molding grade, 10% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness.App..
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Wellman Wellamid® XT1482-N Impact Modified Nylon 66, Lubricated & Heat Stabilized Typical Applications: Automotive fasteners, living hinge, head lamp adjustment devices, ink pen components, wire separators, hardware components, window installation clips, safety equipment.Data pro..
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Total PPH 12020 Polypropylene Homopolymer, Injection Molding Polypropylene PPH 12020 is a clarified high fluidity homopolymer with a melt flow index of 60 g/10 min.Polypropylene PPH 12020 has been designed with a very high stiffness and an outstanding transpa..
Flexural Modulus	1.80 GPa	261 ksi	ASTM D790
Lubrizol Isoplast® 101 Engineering Thermoplastic Polyurethane Resin ISOPLAST® 101 is an engineering thermoplastic polyurethane resin.Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product li..
Flexural Modulus	1.80 GPa	261 ksi	ASTM D790
Eastman Eastar CN015 Copolyester, High Flow Grade with Mold Release Applications:CompactsCosmetic jar capsCosmetic jarsCosmetics/personal care packagingFragrance capsFragrance packagingLip gloss containersLipstick containersPersonal care bottlesKey Attributes:Abilit..
Flexural Modulus	1.80 GPa	261 ksi	ASTM D790
Eastman Eastar MN004 Copolyester Eastar Copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN004 contains a mold release.Appl..
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min, 4 mm; ISO 178
Chi Mei Kibiton® PB-5925 SBC Transparency, high stiffness, injection grade
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min; ISO 178
Chi Mei Polylac® PA-765 ABS - Flame Retardant F.R. High Flow
Flexural Modulus	1.80 GPa	261 ksi	SAE J949
Azdel SuperLite® SL550600-100 PP Resin Matrix / 55% Glass Fiber (1.5 mm Molded Thickness) AZDEL SuperLite® SL550600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic..
Flexural Modulus	1.80 GPa	261 ksi	ASTM D790
A. Schulman ComAlloy Comtuf® 618 Nylon 6, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.15% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i..
Flexural Modulus	1.80 GPa @Temperature 23.0 °C	261 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPC T1020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Modulus	1.80 GPa	261 ksi	ASTM D790
Tipco Tipcolene® HR 7222 - 25% Talc/Mineral Reinforced, Impact Modified Polypropylene Copolymer Compound 25% Mineral Reinforced, Impact Modified PP Copolymer BlendApplications: Automotive InteriorsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Valox® VX3608C PBT (Europe-Africa-Middle East) VALOX VX3608C is an impact modified, flame retardant PBT+PC injection moulding resin. Application: electrical enclosures. This grade is 3607U with reduced oxygen index.This data was supplied by SABI..