Mechanical Properties	Metric	English	Comments
Flexural Modulus	3.95 GPa	573 ksi	ISO 178
Radici Radilon® AERV1906 LK (dry) Nylon 66 Glass-fiber reinforced with high impact strength, heat stabilizedInformation provided by Radici group.
Flexural Modulus	3.95 GPa	573 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Lubricomp DFP22 PC LNP* DFP22 is a Polycarbonate base resin containing glass fiber and PTFE/Silicone Lubricants. Characteristic of this grade is: Internally Lubricated.This data was supplied by SABIC-IP for the Amer..
Flexural Modulus	3.95 GPa	573 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL42 PC LNP* Lubricomp* DFL-4042 a compound based on Polycarbonate resin containing 10% Glass Fiber, 20% PTFE. Added features include: Internally Lubricated.
Flexural Modulus	3.95 GPa	573 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP RBL36L PA 66 LNP* LUBRICOMP* RBL36L is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features s of this grade are: Low Extractable, Wear Resistant.
Flexural Modulus	3.95 GPa	573 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DF002 PC LNP THERMOCOMP* DF002 is a compound based on Polycarbonate resin containing 10% Glass Fiber.
Flexural Modulus	3.95 GPa	573 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DF002H PC LNP THERMOCOMP* DF002H is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added feature includes: Healthcare.
Flexural Modulus	3.95 GPa	573 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP RF003H PA 66 LNP* THERMOCOMP* RF003H is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare.
Flexural Modulus	3.95 GPa	573 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP RF003XXH PA 66 LNP* THERMOCOMP* RF003XXH is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare.
Flexural Modulus	3.95 GPa	573 ksi	ASTM-D790
Polyram PlusTek PB302G3 Nylon 6, 15% Glass Fiber 15% glass-fiber reinforced, heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	3.95 GPa	573 ksi	ISO 178-93
Wellman Wellamid® GFT13-66 XE-NBK1 13% Glass Fiber Reinforced, Impact Modified Nylon 66 Description: Glass Fiber Reinforced, Impact Modified Nylon 66Information provided by Wellman.
Flexural Modulus	3.95 GPa	573 ksi	ISO 178-93
Wellman Wellamid® GS1684-WBK1 25% Glass Sphere Filled Nylon 66 Description: Glass Sphere Filled Nylon 66Information provided by Wellman.
Flexural Modulus	3.95 GPa	573 ksi	ASTM-D790
Polyram RamTough RZ300G13 Polycarbonate, 13% Glass Fiber 13% glass fiber reinforced polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind.