Polymer Property : Flexural Modulus = 670 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	4.62 GPa	670 ksi	ASTM D790
PolyOne Maxxam™ NT-818.G002-1000 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Flexural Modulus	4.62 GPa	670 ksi	ASTM D790
PolyOne Maxxam™ NT-818.G002-8000 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Flexural Modulus	4.62 GPa @Temperature 175 °C	670 ksi @Temperature 347 °F	ISO 178
Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA) (Unverified Data**) Amodel AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrar..
Flexural Modulus	4.62 GPa @Temperature 150 °C	670 ksi @Temperature 302 °F	ISO 178
Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Typical applications include ..
Flexural Modulus	4.62 GPa	670 ksi	6.4 mm; ASTM D790
SABIC Innovative Plastics NORYL ZM3640 PPE+PS (Asia Pacific)
Flexural Modulus	4.62 GPa @Temperature 175 Â°C	670 ksi @Temperature 347 Â°F	ISO 178
Solvay Specialty Polymers AmodelÂ® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both in..
Flexural Modulus	4.62 GPa @Temperature 150 Â°C	670 ksi @Temperature 302 Â°F	ISO 178
Solvay Specialty Polymers AmodelÂ® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samp..
Flexural Modulus	4.62 GPa	670 ksi	ASTM D790
Techmer ES HiFillÂ® PA4/6 GF30 HS BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedUL File Number: E157318Appearance: Bla..
Flexural Modulus	4.62 GPa	670 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF002XXH PA 66 LNP THERMOCOMP* RF002XXH is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added feature of this material includes: Healthcare.
Flexural Modulus	4.62 GPa	670 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp WB008 PBT LNP* Thermocomp* WB008 is a compound based on Thermoplastic Polyester (PBT) containing Glass Beads.This data was supplied by SABIC-IP for the Americas region.
Flexural Modulus	4.62 GPa	670 ksi	ASTM D790
Ensinger Tecatron® XP-170 Compression Molded PPS Compound, EWS Filled Ensinger Special Polymers has over twenty different grades of TECATRON PPS available. Custom formulations can be blended to suit specific applications. Compression molding is amenable to short run p..
Flexural Modulus	4.62 GPa	670 ksi	ASTM D790
Clariant Renol 66G15BL-195 Blue Nylon 66, 15% Glass Fiber Reinforced Data provided by Clariant Masterbatches
Flexural Modulus	4.62 GPa @Temperature 150 °C	670 ksi @Temperature 302 °F	ISO 178
Solvay Specialty Polymers Amodel® AS-4133 HN Polyphthalamide (PPA), Dry, 33% Glass Fiber Reinforcement, Heat Stabilizer Amodel AS-4133 HN polyphthalamide (PPA) is a non-lubricated, heat stabilized grade that offers fast cycle times and is hot-water moldable. Typical applications include electrical and electronic comp..