Polymer Property : Flexural Modulus = 7.92 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	7.92 GPa	1150 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC LNP* Lubricomp* DFL16E is a compound based on Polycarbonate resin containing 30% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated, Easy Molding.
Flexural Modulus	7.92 GPa	1150 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC (Asia Pacific) LNP* Lubricomp* DFL16E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Easy Molding.
Flexural Modulus	7.92 GPa	1150 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP IFL36 PA6.12 LNP LUBRICOMP* IFL36 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Flexural Modulus	7.92 GPa	1150 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP REL22 PA 66 LNP* LUBRICOMP* REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive.
Flexural Modulus	7.92 GPa	1150 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP SFP36 PA12 LNP* LUBRICOMP* SFP36 is a compound based on Nylon 12 resin containing 30% Glass Fiber 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
Flexural Modulus	7.92 GPa	1150 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP XFL36 AMORPHOUS POLYAMIDE LNP* LUBRICOMP* XFL36 is a compound based on Amorphous Nylon containing 30% Glass Fiber and 15% PTFE. Added feature of this material is: Wear Resistant.
Flexural Modulus	7.92 GPa	1150 ksi	6.4 mm; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM4025 PPE+HIPS (Europe-Africa-Middle East) LNP* Thermocomp* Noryl_FM4025 compound is GR/MR 40%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness.
Flexural Modulus	7.92 GPa	1150 ksi	6.4 mm; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM4025 PPE+PS LNP* Thermocomp* Noryl_FM4025 compound is GR/MR 40%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness.
Flexural Modulus	7.92 GPa	1150 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON LX00797C PEEK LNP* STAT-KON* LX00797C is a compound based on Polyetheretherketone containing Proprietary Filler(s). Added features of this material include: ristics of this grade are: Clean Compounding System, ..