- Polymer Property : Charpy Impact, Unnotched = 116 ft-lb
Polymer Property : Charpy Impact, Unnotched = 116 ft-lb Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Charpy Impact, Unnotched | 157 J @Temperature 677 °C |
116 ft-lb @Temperature 1250 °F |
Longitudinal |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Copyright © lookpolymers.com All Rights Reserved