Polymer Property : Flexural Strength = 25000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	172 MPa @Temperature 93.3 °C	25000 psi @Temperature 200 °F	Dry; ASTM D790
Park Electrochemical Nelcote® V-341 Polybutadiene Prepreg, 503 Quartz Reinforced Nelcote® V-341 is Polybutadiene resin system designed to provide excellent electrical properties in demanding airborne, shipboard, and undersea applications.Key Features and Benefits:Extremely low ..
Flexural Strength	172 MPa @Thickness 6.35 mm	25000 psi @Thickness 0.250 in	LW
Industrial Laminates/Norplex MC603 Paper Base Laminate (discontinued **) Description: MC603 is constructed from electrical grade of kraft paper and a specially modified phenolic resin system, and is designed to be used in tap changers, coil support plates and terminal pa..
Flexural Strength	172 MPa @Thickness 1.57 mm	25000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP600 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is most commonly used for drill entry material in the PCB industry. Thickness Tested: 0.062"..
Flexural Strength	172 MPa @Thickness 1.57 mm	25000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP602 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. It is typically hot punched for numerous low voltage, less than 250 volts, electrical applications.Thickne..
Flexural Strength	172 MPa @Thickness 1.57 mm	25000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP605 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is normally used in the printed circuit board industry as a backup for the drilling operatio..
Flexural Strength	172 MPa @Thickness 1.57 mm	25000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP639 Paper Base Laminate Description: Economical paper reinforced laminate developed with capacity to withstand temperatures to 150Â° C without blistering. High compressive strength and low moisture absorption.Thickness T..
Flexural Strength	172 MPa @Thickness 1.57 mm	25000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP843 Paper Base Laminate Description: Paper reinforced phenolic grade with controlled conductivity. Mechanical strength similar to NP611. NP843 has conductive surfaces only, as compared to NP842, which is conductive through..