Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 500 MPa @Thickness >=1.60 mm, Temperature 50.0 °C |
72500 psi @Thickness >=0.0630 in, Temperature 122 °F |
Perpendicular to laminations; EN 60893 |
HOS-Technik Homide 250 Bismaleimide Resin Homide 250 is a prepolymer bismaleimide resin system with a low softening range of 90-125°C supplied in powder form. The resin can be cured thermally to create a cross-linked thermoset with excel.. |
|||
Flexural Strength | 500 MPa @Thickness >=1.60 mm, Temperature 20.0 °C |
72500 psi @Thickness >=0.0630 in, Temperature 68.0 °F |
Perpendicular to laminations; EN 60893 |
HOS-Technik Homide 250 Bismaleimide Resin Homide 250 is a prepolymer bismaleimide resin system with a low softening range of 90-125°C supplied in powder form. The resin can be cured thermally to create a cross-linked thermoset with excel.. |
|||
Flexural Strength | 500 MPa @Thickness >=1.50 mm |
72500 psi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 |
Elektro-Isola G-Etronax EP S Epoxy, Glass Fabric Reinforcement, Green, Sheets Description: Particularly good electrical and mechanical properties by continuous use, even at high temperatures. Very good chemical resistance. Engineering and insulation material in electrical mac.. |
|||
Flexural Strength | 500 MPa @Treatment Temp. 20.0 °C, Time 3600 sec |
72500 psi @Treatment Temp. 68.0 °F, Time 1.00 hour |
ISO 178; IEC/EN 60893-2 5.1 |
Elektro-Isola G-Etronax PI Polyimide, Glass Fabric Reinforcement, Dark Brown, Sheets Description: The most temperature-resistant material of all types. Retains its outstanding mechanical properties even at very high application temperatures. Applications: Used as thermal insulation .. |