Polymer Property : Shear Strength = 11.7 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	11.7 MPa @Temperature 93.3 Â°C	1700 psi @Temperature 200 Â°F	ASTM D732
Greene Tweed AvalonÂ® 56 PTFE PTFE is used in many pharmaceutical-sealing applications. Its chemical inertness and ultra-low level extractables provide pharmaceutical process and validation engineers with a safe material to use..
Shear Strength	11.7 MPa @Temperature 93.3 °C	1700 psi @Temperature 200 °F	Lap Shear
Hexcel® Redux® 335M Adhesive film for bonding metallic and composite components (0.06 psf) Redux 335 is a film adhesive curing at 250F. It is available in a range of standard areal weights from 0.015 to 0.06 psf. It is available either unsupported or with knitted and/or matt carrier for a..
Shear Strength	11.7 MPa @Temperature 121 °C	1700 psi @Temperature 250 °F	Aluminum Overlap
3M Scotch-Weld™ 2214 Hi-Dense Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Dense is a deareted version of Scotch-Weld adhesive 2214 regular for use where a very dense, void free bondline is required. One part 250°F (121°C) curing 100% ..
Shear Strength	11.7 MPa @Time 259000 sec	1690 psi @Time 72.0 hour	Overlap, Maple conditioned for 7 days AT RT/50% RH
3M Scotch-Weld™ EZ250015 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds well to wood and wood bases surfaces as w..
Shear Strength	11.7 MPa @Temperature 23.0 °C	1700 psi @Temperature 73.4 °F	Overlap, FRP, Substrate Failure
3M Scotch-Weld™ TE200 Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as ..
Shear Strength	11.7 MPa @Temperature 23.0 °C	1690 psi @Temperature 73.4 °F	Overlap, FRP
3M Scotch-Weld™ TS115 HGS Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as ..
Shear Strength	11.7 - 12.1 MPa @Temperature 23.0 °C	1700 - 1750 psi @Temperature 73.4 °F	Overlap Copper/Copper (MEK Wiped); ASTM D1002-72
3M Scotch-Weld™ DP270 Black Structural Adhesive Rigid potting compound, Non-corrosiveInformation provided by 3M
Shear Strength	11.7 - 12.1 MPa @Temperature 23.0 °C	1700 - 1750 psi @Temperature 73.4 °F	Overlap Copper/Copper (MEK Wiped); ASTM D1002-72
3M Scotch-Weld™ DP270 Clear Structural Adhesive Rigid potting compound, Non-corrosiveInformation provided by 3M