Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 0.862 MPa @Temperature 66.0 °C |
125 psi @Temperature 151 °F |
1/8" Birch/High-Pressure Laminate, aged 9 mo |
3M Fastbond™ 30-NF Contact Adhesive 3M Fastbond™ Contact Adhesive 30-NF and 30H-NF are water-dispersed, sprayable contact adhesives for high immediate bond strength n long bonding range.Information provided by 3M |
|||
Shear Strength | 0.862 MPa @Temperature 66.0 °C |
125 psi @Temperature 151 °F |
1/8" Birch/High-Pressure Laminate, aged 9 mo |
3M Fastbond™ 30H-NF Contact Adhesive 3M Fastbond™ Contact Adhesive 30-NF and 30H-NF are water-dispersed, sprayable contact adhesives for high immediate bond strength n long bonding range.Information provided by 3M |
|||
Shear Strength | 0.862 MPa @Temperature 82.0 °C |
125 psi @Temperature 180 °F |
Overlap, Lexan |
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 0.862 MPa @Temperature 82.0 °C |
125 psi @Temperature 180 °F |
Overlap, Lexan |
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 0.862 MPa @Temperature 82.0 °C |
125 psi @Temperature 180 °F |
Overlap, Lexan |
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |