Polymer Property : Vicat Softening Point = 44.0 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Vicat Softening Point	44.0 °C @Load 1.00 kg	111 °F @Load 2.20 lb	ISO 306/A
Polimeri Europa Greenflex® ML 60 Ethylene Vinyl Acetate Copolymer - Injection Molding, Compounding & Extrusion Greenflex ML 60 is an ethylene vinyl acetate copolymer (EVA) for injection molding, compounding and extrusion. Items produced with Greenflex ML 60 show very high elasticity.Main Applications: Gree..
Vicat Softening Point	44.0 - 96.0 °C	111 - 205 °F	Average value: 78.3 °C Grade Count:143
Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate Copolymer (EVA), Film Grade". Each property range of values reported is minimum a..
Vicat Softening Point	44.0 Â°C	111 Â°F	A; ISO 306
FKuR Kunststoff Bio-FlexÂ® A 4100 CL Compostable PLA Blend The BIO-FLEXÂ® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEXÂ® does not contain any sta..
Vicat Softening Point	44.0 °C	111 °F
BASF Procom® D 1118 Polypropylene Data was collected by ISO methods and provided by BASF.
Vicat Softening Point	44.0 °C	111 °F	ASTM D1525
Westlake EMAC® SP2403 24% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2403 is a 24% EMA copolymer designed for extrusion coating, tie-layers, compounding, and extrusions where flexibility, compatibility, low heat seal temperatures, or high coefficien..
Vicat Softening Point	44.0 °C	111 °F	1000g; ASTM D-1525
ExxonMobil Escorene® LD-724 High EVA Compounding Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer resin for specialty compounding applications. Outstanding heat sealability along with excellent strength properties ..