Polymer Property : Specific Heat Capacity = 0.172 BTU/lb-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Specific Heat Capacity 0.720 J/g-°C
0.172 BTU/lb-°F
calculated
Rogers Corporation TMM® TMM101 Ceramic Thermoset Polymer Composite
TMM® Thermoset microwave materials are ceramic thermoset polymer composites designed for high plate-thru-hole reliability stripline and microstrip applications. The electrical and mechanical prope..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy, annealed plate
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy, solution annealed sheet
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Specific Heat Capacity 0.719 J/g-°C

@Temperature 1100 °C
 0.172 BTU/lb-°F

@Temperature 2010 °F
Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Copyright © lookpolymers.com All Rights Reserved