Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 107 °C @Thickness 3.20 mm |
225 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® LG9000 PC+ABS PC+ABS blend, low gloss and UV-stable, suitable for automotive interior applications. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 107 °C @Thickness 3.20 mm |
225 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® LG9000 PC+ABS (Asia Pacific) PC+ABS blend, low gloss and UV-stable, suitable for automotive interior applications. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 107 °C @Thickness 3.20 mm |
225 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® MC8002 PC+ABS AUTOMOTIVE. Low viscosity, high impact and ductility. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 107 °C @Thickness 3.20 mm |
225 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® MC8002 PC+ABS (Asia Pacific) AUTOMOTIVE. Low viscosity, high impact and ductility. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 107 °C @Thickness 3.20 mm |
225 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
Styron PULSEâ„¢ 2100 LG PC/ABS Engineering Resin Overview: PULSE 2100LG Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 107 °C @Thickness 6.40 mm |
225 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics Noryl EN110 PPE+PS (Asia Pacific) Medium heat, extrusion grade PPO/HIPS alloy.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 107 °C @Thickness 6.40 mm |
225 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics NORYL EN95 PPE+PS (Asia Pacific) Low heat, extrusion grade PPO/HIPS alloy. |