Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 10.52 µm/m-°C @Temperature 20.0 - 100 °C |
5.844 µin/in-°F @Temperature 68.0 - 212 °F |
409 HP™ |
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 14% Cold Work AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze.. |
|||
CTE, linear | 10.52 µm/m-°C @Temperature 20.0 - 100 °C |
5.844 µin/in-°F @Temperature 68.0 - 212 °F |
409 HP™ |
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 16.4% Cold Work AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze.. |
|||
CTE, linear | 10.52 µm/m-°C @Temperature 20.0 - 100 °C |
5.844 µin/in-°F @Temperature 68.0 - 212 °F |
409 HP™ |
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 2.9% Cold Work AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze.. |
|||
CTE, linear | 10.52 µm/m-°C @Temperature 20.0 - 100 °C |
5.844 µin/in-°F @Temperature 68.0 - 212 °F |
409 HP™ |
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 34.5% Cold Work AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze.. |
|||
CTE, linear | 10.52 µm/m-°C @Temperature 20.0 - 100 °C |
5.844 µin/in-°F @Temperature 68.0 - 212 °F |
409 HP™ |
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 43.6% Cold Work AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze.. |
|||
CTE, linear | 10.52 µm/m-°C @Temperature 20.0 - 100 °C |
5.844 µin/in-°F @Temperature 68.0 - 212 °F |
409 HP™ |
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 8.5% Cold Work AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze.. |
|||
CTE, linear | 10.52 µm/m-°C @Temperature 20.0 - 100 °C |
5.844 µin/in-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum AL 409HP™ Ferritic Stainless Steel, UNS S40930 Type 409 ferritic stainless steel was introduced by Allegheny Ludlum in 1961 to provide improved oxidation and corrosion resistance for automotive exhaust systems in comparison to carbon automotive .. |
|||
CTE, linear | 10.52 µm/m-°C @Temperature 20.0 - 100 °C |
5.844 µin/in-°F @Temperature 68.0 - 212 °F |
409 HP™ |
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 20% Cold Work AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze.. |
|||
CTE, linear | 10.52 µm/m-°C @Temperature 20.0 - 100 °C |
5.844 µin/in-°F @Temperature 68.0 - 212 °F |
409 HP™ |
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze.. |