Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 200 °C |
6.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
Kennametal Stellite Nucalloy® 488V High-Silicon Nickel-Base Hardfacing Alloy Applications include diesel engine valves, and injection mold screws.Nucalloy® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinati.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 0.000 - 400 °C |
6.44 µin/in-°F @Temperature 32.0 - 752 °F |
|
Industeel VIRGO 15.5PH 15Cr-5Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (480°C (900°F) - 1 hour - air cooling) Description: Alloy VIRGO 15.5 PH is a precipitation hardening martensitic stainless steel with 15% Cr, 5% Ni, 3.5% Cu and 0.3% Nb/Cb. The grade combines high mechanical properties and medium corrosi.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 300 °C |
6.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 300 °C |
6.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 300 °C |
6.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 300 °C |
6.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 300 °C |
6.44 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 400 °C |
6.44 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® B-3® alloy, 20% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 400 °C |
6.44 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 400 °C |
6.44 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® B-3® alloy, 50% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 100 °C |
6.44 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 100 °C |
6.44 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 100 °C |
6.44 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate, Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 100 °C |
6.44 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 100 °C |
6.44 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 38.0 - 260 °C |
6.44 µin/in-°F @Temperature 100 - 500 °F |
|
Latrobe Lescalloy® 52100 VAC-ARC High Performance Bearing Steel LESCALLOY 52100 VAC-ARC is a deep hardening alloy steel used for aircraft bearings and other high stressed parts where good rolling contact fatigue strength is required at operating temperatures bel.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 600 °C |
6.44 µin/in-°F @Temperature 68.0 - 1110 °F |
DIN EN 821-1 |
CeramTec MZ 111 Zirconia, ZrO2-Y2O3 MZ 111 is a yttria-stabilized tetragonal zirconia used in dental applications. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 200 °C |
6.44 µin/in-°F @Temperature 68.0 - 392 °F |
after high temperature tempering |
Assab Steels ASSAB 88 Cold Work Steel ASSAB 88 (SLEIPNER) is a chromium-molybdenum-vanadium alloyed tool steel which is characterized by:Good wear resistanceGood chipping resistanceHigh compressive strengthHigh hardness (>60HRC) after h.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 200 °C |
6.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
ATI Allegheny Ludlum 425 Mod Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 200 °C |
6.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 538°C Temper Allegheny Ludlum Type 425 Mod is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stai.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 200 °C |
6.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 316°C Temper Allegheny Ludlum Type 425 Mod is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stai.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 500 °C |
6.44 µin/in-°F @Temperature 68.0 - 932 °F |
|
ATI Allegheny Ludlum AL 468™ Dual Stabilized- Low Titanium Stainless Steel Characteristics:good corrosion resistance in a wide range of environments, can be used in annealed cold formed or as-welded conditions. Applications: used in place of Type 304 in an oxidizing when .. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 500 °C |
6.44 µin/in-°F @Temperature 68.0 - 932 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 70% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature <=649 °C |
6.44 µin/in-°F @Temperature <=1200 °F |
|
AK Steel 410 Cb Martensitic Stainless steel AK Steel 410 Cb is an improved version of standard Type 410. The addition of columbium offers 3 major advantages: 1) Greater ease in heat treating, 2) Higher strength and toughness, 3) Improved gra.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 200 °C |
6.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 482°C Temper Allegheny Ludlum Type 425 Mod is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stai.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 25.0 - 400 °C |
6.44 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes Hastelloy® B-3® alloy, heat treated at 1065°C, rapid quenched The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ea.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 600 °C |
6.44 µin/in-°F @Temperature 68.0 - 1110 °F |
|
ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Annealed Allegheny Ludlum Type 410 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainles.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 600 °C |
6.44 µin/in-°F @Temperature 68.0 - 1110 °F |
|
ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 288°C Temper Allegheny Ludlum Type 410 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainles.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 500 °C |
6.44 µin/in-°F @Temperature 68.0 - 932 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 50% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
CTE, linear | 11.6 µm/m-°C @Temperature 20.0 - 450 °C |
6.44 µin/in-°F @Temperature 68.0 - 842 °F |
|
Schmolz + Bickenbach Formadur® 2316/2316 ESR Plastic Mold Steel Increased corrosion resistance in comparison to Formadur 2083, good polishability. Usually this grade is supplied quenched and tempered to 300 HBApplications: Molds for processing plastics with corr.. |