Polymer Property : CTE, linear = 13.9 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.9 µm/m-°C @Temperature 0.000 - 100 °C |
7.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 0.000 - 100 °C |
7.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 0.000 - 100 °C |
7.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 0.000 - 100 °C |
7.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 700.0 °C |
7.72 µin/in-°F @Temperature 68.0 - 1292 °F |
|
| International Mold Steel DH2F Pre-Hardened H13-Type Mold Steel Description: DH2F is one of the best machining pre-hardened H13-type steels available.Unique Characteristics: 38-42 HRc hardness.Through hardened for exceptional dimensional stability.Cuts mold maki.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 500 °C |
7.72 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Haynes Waspaloy™ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, go.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 25.0 - 900 °C |
7.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 10% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 25.0 - 900 °C |
7.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 20% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 25.0 - 900 °C |
7.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 25.0 - 900 °C |
7.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes Hastelloy® B-3® alloy, 30% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 30% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 50% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, 60% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, SMAW weld, C-22 base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 40% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 5% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1200°F (650°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain siz.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 93.0 °C |
7.72 µin/in-°F @Temperature 68.0 - 199 °F |
|
| ATI Allegheny Ludlum AL 400™ Nickel-Base Alloy, Heavily Cold Rolled Sheet and Strip, UNS N04400 Moderately to faintly magnetic at room temperature. Allegheny Ludlum AL 400 alloy is a ductile nickel-copper alloy with resistance to a variety of corrosive conditions. The alloy is most frequentl.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 20.0 - 93.0 °C |
7.72 µin/in-°F @Temperature 68.0 - 199 °F |
|
| ATI Allegheny Ludlum AL 400™ Nickel-Base Alloy, Annealed Plate, Sheet, and Strip, UNS N04400 Moderately to faintly magnetic at room temperature. Allegheny Ludlum AL 400 alloy is a ductile nickel-copper alloy with resistance to a variety of corrosive conditions. The alloy is most frequentl.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, all-weld metal, GTAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.9 µm/m-°C @Temperature 24.0 - 538 °C |
7.72 µin/in-°F @Temperature 75.2 - 1000 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW weld, 316L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||