- Polymer Property : CTE, linear = 14.2 µm/m-°C
Polymer Property : CTE, linear = 14.2 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.89 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Kennametal Stellite Stellite® 19 Can be machined with carbide tipped tools, but when hardness exceeds Rc55 it is best to grind. Applications include cutting tools, bearing races, guide rolls, and nozzle discs. Excellent resistance .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 625/ Alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Stainless steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy, gas metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy, gas tungsten arc welds, aged 1000 hours at 650°C (1200°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Hastelloy® W alloy, shielded metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 600 °C |
7.89 µin/in-°F @Temperature 1110 °F |
|
| Bohler-Uddeholm BÖHLER M268 VMR® Plastic Mold Steel Description: HBÖHLER M268 VMR is a hardened and tempered plastic mould steel with excellent cleanliness for best polishability. The hardness is constant over the entire cross-section of the steel b.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 199 °C |
7.90 µin/in-°F @Temperature 68.0 - 390 °F |
|
| Carlson 2205 (UNS S31803) Duplex Stainless Steel General DescriptionCarlson Alloy 2205 is a second-generation, nitrogen-alloyed duplex stainless steel (ferritic-austenitic). It offers an excellent combination of both strength and corrosion resist.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 20.0 - 1000 °C |
7.89 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| ATI Allegheny Ludlum Stainless Steel Ohmaloy® 40 Resistance Alloy Ohmaloy 40 alloy is a moderately magnetic, ductile stainless steel having extremely high electrical resistivity. In addition to imparting high electrical resistivity, the aluminum content in these .. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.89 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 14.2 µm/m-°C @Temperature 427 °C |
7.89 µin/in-°F @Temperature 800 °F |
|
| Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |
|||